The above setting achieve the best result that I can have currently (Nozzle = 0.3mm).  After a lot of forum browsing I found that:

Stringing can decrease by,
-Decrease Destring Speed
-Decrease Temperature
-Increase Retraction
-Increase Layer height

For reducing Corner Blobbing,
-Increase Jerk (I don't know what is it)
-Decrease Retraction

Can Chings advise the correct thickness of Offer Ching's 2020 Thin-wall STL?